Guest Article on Sail Making by Todd Bradshaw

Article Source: http://forum.woodenboat.com/showthread.php?200481-Straight-stitching-a-sail

    Author - Todd Bradshaw's Avatar: Todd Bradshaw - Wood B. Good

Re: Straight stitching a sail

Felled seams on modern Dacron would be quite difficult to make, especially on a computer-cut sail because computers cut panels with curved edges instead of broadseaming. Plus, the fabric is awfully stiff for that sort of seam. Two lines of straight stitches can be used (V46 or V69 thread and a #16 or #18 needle and about 8-10 stitches per inch) but as mentioned, it isn't ideal for strength because it is making what are essentially perforated lines on the sail that kind of say "tear here". This is accentuated by the tearing properties of modern, resin-coated Dacron. 

​

Unlike most other fabrics, Dacron's low stretch means that the individual yarns don't help each other out much when stress is applied. Essentially, the first yarn tries to take all the stress (until it breaks) then the second yarn does the same thing and this scenario just repeats over and over, yarn after yarn. This is why I can take a hunk of heavy Dacron sailcloth (12 oz. or better) give it a sharp tug and tear it right in half. Even though it happens quite fast, I'm essentially only having to tear one yarn at a time. Other synthetics, like nylon, work differently. Stress will concentrate on the first yarn, but will also be spread out to some extent to its neighboring yarns. We take advantage of the Dacron's non-stretch properties in order to make sails that will keep their designed shape in use, but we make allowances to preserve it's strength where we can. The typical zig-zag puts maybe a quarter of an inch or more between the needle holes and yields seams with a higher tear strength and less in the way of a perforated line.

​

The other thing that really helps is double-sided seam basting tape. Not only does it instantly make sewing easier, keeping panels aligned for seaming, but it adds a tremendous amount of seam strength. Once the adhesive has had a week or two to completely cure (dwell time) it makes seams that are hard to disassemble without messing up the cloth. 

​

The various types of seams would probably grade out like this:

​

Strongest - Seam tape with two lines of zig-zag stitching (maybe 3 lines, with wider seam overlaps, and heavier cloth on big offshore sails).

​

Production Sails - Many of these are now sewn with a 3-step machine, which sews a single line of stitches in a wider zig-zag pattern, but each zig or zag is actually made up from three straight stitches. Less strength, but the sail only needs half as many passes through the sewing machine, making them cheaper to build. Good ones are seam-taped first. Not so good ones are seam "basted" by pricking the fabric with a hot knife with a tiny needle-like tip every few inches, melting the layers together. It saves a substantial amount of time, but adds no additional strength to the seams beside that of the stitches.

​

Straight stitching - Even when tape-basted and double-stitched, the lines of perforations are still a concern, but they still may be as good or better than a needle-basted 3-step seam because the tape adds so much strength to the seams. If straight stitching is all you have and you aren't planning on crossing any oceans, you can probably get away with it. Sailrite's plotter cuts with a spinning cutting wheel that generates enough heat to slightly melt the cloth - so the fact that you aren't pinning down the cut edges of the seams with a zig-zag probably won't be a problem. On hand-cut edges, it likely would cause some raveling. 

​

Lap-feld seams with two lines of straight stitching were (still are) the norm on cotton sails and are quite strong, but cotton has far more stretch than Dacron, so the perforated lines aren't a problem. They also work great on nylon and other soft synthetics (backpacking tents, clothing, and even hot-air balloons - we used to be required to use them for patching balloons when I worked on them). Zig-zag stitching is less popular on these things because the stitches are easier to snag and tear.